The Dispersion of Fine Chitosan Particles by Beads-Milling
Emma Rochima, Safira Utami, Herman Hamdani, Sundoro Yoga Azhary, Danar Praseptiangga, I Made Joni, Camellia Panatarani
Universitas Padjadjaran, The 1st International Conference and Exhibition on Powder Technology Indonesia (ICePTi) 2017, AIP Conf. Proc. 1927, 030032-1–030032-4; https://doi.org/10.1063/1.5021225, Published by AIP Publishing. 978-0-7354-1619-2/$30.00
Bahasa Inggris
Universitas Padjadjaran, The 1st International Conference and Exhibition on Powder Technology Indonesia (ICePTi) 2017, AIP Conf. Proc. 1927, 030032-1–030032-4; https://doi.org/10.1063/1.5021225, Published by AIP Publishing. 978-0-7354-1619-2/$30.00
Fine Chitosan Particles
This research aimed to produce fine chitosan particles from a crab shell waste by beads-milling method by two different concentration of PEG as dispersing agent (150 and 300 wt. %). The characterization was performed to obtain the size and size distribution, the characteristics of functional groups and the degree of deacetylation. The results showed that the chitosan fine particles was obtained with a milling time 120 minutes with the best concentration of PEG 400 150 wt. %. The average particle size of the as-prepared suspension is 584 nm after addition of acetic acid solution (1%, v/v). Beads milling process did not change the glucosamine and N-acetylglucosamine content on chitosan structure which is indicated by degree of deacetylation higher than 70%. It was concluded that beads milling process can be applied to prepare chitosan fineparticles by proper adjustment in the milling time, pH and dosage of dispersing agent.