The Use of TiO2-SiO2 in Photocatalytic Process To Degdrade Toxic and Dangerous Waste
Lia Destriarti, Roekmiati Tjokronegoro, Diana Rakhmawaty and Rudiyansyah
Unpad
Inggris
Lia Destriarti, Roekmiati Tjokronegoro, Diana Rakhmawaty and Rudiyansyah
Cr(VI), LAS, Phenol, Photocatalyst, TiO2-SiO2
This study was conducted to investigate the use of TiO2 immobilized on Si02 (Ti02-Si02) in a photocatalytic process to degrade toxic industrial waste, phenol, linear alkylbenzene sulfonate (LAS), and Cr(VI), which is dangerous for humans and the environment. Titanium dioxide (Ti02), as a photocatalyst, can make the solution become turbid. Thus, Ti02-Si02 was used to increase the possibility of ultraviolet (UV) transmission. The phenol and LAS levels were measured with the Indonesian National Standard (INS) while the Cr(VI) level was determined with the colorimetric method. The activity test for the catalyst in suspension and immobilization against phenol showed that Ti02-Si02 was more active than Ti02. By using the photocatalytic process with the Ti02-Si02 photocatalyst for 8 h, degradation of phenol and LAS reached 50% as a single compound and 12% as a mixture. However, Ti02-SiO2 did not decrease Cr(VI).
Penggunaan Ti02-Si02 dalam Proses Fotokatalisis untuk Mendegradasi Limbah Beracun dan Berbahaya. Penelitian dilakukan untuk mengamati penggunaan Ti02-Si02 dalam proses fotokatalitik guna mendegradasi fenol, linear alkylbenzene sulfonate (LAS), dan Cr(VI), dimana ketiganya merupakan limbah industri yang beracun dan berbahaya bagi manusia dan makhluk hidup. Titanium dioksida (Ti02), merupakan suatu fotokatalis yang dapat membuat larutan menjadi keruh. Ti02-Si02 digunakan untuk meningkatkan peluang transmisi ultraviolet (UV). Kadar fenol dan LAS diukur berdasarkan Standar Nasional Indonesia, sedangkan pengukuran kadar Cr(VI) dengan metode kolorimetri. Uji aktivitas untuk katalis bentuk suspensi dan imobilisasi terhadap fenol menunjukkan bahwa Ti02-Si02 lebih aktif dibandingkan TiO2 murni. Degradasi fenol dan LAS secara Wilmal dengan fotokatalisis selama 8 jam dapat mencapai 50%, degradasi fenol dan LAS dapat mencapai 12% untuk pengolahan secara campuran. Namun demikian, katalis Ti02-Si02 tidak mendegradasi Cr(VI).